The high wearing resistance of the samples after hydrocooling and air cooling was partially attributed to martensite transformation and work-hardening.

经水冷和空冷的试样具有高的重要原因是其在损过程中诱发了马氏体相变,出现加工硬化现象。

It was reported that the detwinning stress in martensite of Ti-Ni alloys increases with increasing annealing temperature, but the reason for such a strange behavior has remained unclear.

有报道Ti-Ni合金的去孪晶应力随着退火温度的升高而升高，但是造成这一现象的原因并。

It holds that main causes promoting crack on martensite stainless steel are gross martensite and crystal boundary carburet and secondary phase distributed along crystal boundary.

文章认为，粗大的马氏体组织、晶界碳化物以及沿晶界分布的“第二相”组织是促使马氏体锈钢产生裂纹的主要原因。